KFRP Central Core for Fiber Optical Cables from China manufacturer - Wuxi Dobest Communication Equipment Co.,Ltd

KFRP Central Core for Fiber Optical Cables

Price:	30.0 USD
Payment Terms:	T/T,L/C
Place of Origin:	Jiangsu, China (Mainland)


	Add to My Favorites
HiSupplier Escrow	Share \|

Product Detail

Means of Transport: Ocean,Land,Air

Packing: Robbin and wooden pallets

Brand Name: DOBEST

Diameter: 0.5mm

Production Capacity: 150000kilometers/month

Delivery Date: Within 30 days

Application: Fiber Optical Cables streng...

Φ0.40mm Φ0.50mm×Φ0.58mm
Φ0.45mm Φ0.62mm×Φ0.68mm

0.5mm KFRP Central Core for Fiber Optical Cables:

1.Product Specification:

Φ0.40mm Φ0.50mm×Φ0.58mm

Φ0.45mm Φ0.62mm×Φ0.68mm

2. Features:

1) Light weight and high strength: KFRP has the characteristics of low density and high strength. Its ratio of strength and modulus are higher than those of steel wire and GFRP;

2) Low expansion: KFRP has a lower coefficient of thermal expansion than steel wire and GFRP in a wide range of temperature;

3) Impact and break resistance: KFRP has much higher tensile strength (≥1700Mpa). Even it is broken, the remained tensile strength could be 1300Mpa;

4) Good flexibility: KFRP is flexible and easy to be bent. Its minimum bending diameter is 24 times of the diameter of KFRP rod;

5) Good aesthetic and flexible, especially for the indoor layout.

3. KFRP technical performance indicators:

NO.	Item		Unit	Index
1	Diameter Tolerance	Body	mm	±0.05
		Coating
2	Non-circularity	Body	%	≤5.0
		Coating
3	Minimum Bending Property		--	Bending diameter:10D, surface with no bur, cracks and break
4	Tensile Strength		Mpa	≥1700
5	Tensile Modulus		Gpa	≥52
6	High temperature bending test (80℃,24h)		--	Bending diameter:30D, surface with no bur, cracks and break
7	Low temperature bending test (-40℃,24h)		--	Surface with no bur, cracks and break
	Note1: For KFRP with coating, it only considers the diameter tolerancea and non-circularity of coating Note 2: D represents the body of KFRP itself Note 3: Bending life of material is to research.